Detail produk:
|
| Nama: | Pita Fecral 0Cr13Al4 Fecral Alloy strip untuk elemen panas otomasi rumah | Bahan: | Pita Fecral 0Cr13Al4 |
|---|---|---|---|
| Warna: | abu-abu | Pengiriman: | Tergantung pada kuantitas |
| Permukaan: | Cerah | ||
| Menyorot: | kawat pemanas listrik,kawat suhu tinggi |
||
Spesifikasi
Nilai: 1Cr13AL4, 0Cr15AL5, 0Cr23AL5, 0Cr25AL5, 0Cr21AL6Nb0Cr27AL7Mo2
Ukuran: Kawat: 0.15 ~ 10mm
Bar: 12 ~ 120mm
| Paduan Kinerja Nomenklatur | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Komposisi kimia utama | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Kembali | tepat | tepat | tepat | tepat | tepat | tepat | tepat | |
| Fe | Beristirahat | Beristirahat | Beristirahat | Beristirahat | Beristirahat | Beristirahat | Beristirahat | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Maks. temp layanan berkelanjutan. elemen (° C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Tahanan pada 20ºC (μΩ · m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Kepadatan (g / cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Konduktivitas termal (KJ / m · h · ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | - | |
| Koefisien ekspansi saluran (α × 10-6 / ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Perkiraan titik lebur (ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Kekuatan tarik (N / mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Perpanjangan putus (%) | > 16 | > 12 | > 12 | > 12 | > 12 | > 12 | > 10 | |
| Variasi area (%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Ulangi frekuensi Bending (F / R) | > 5 | > 5 | > 5 | > 5 | > 5 | > 5 | > 5 | |
| Kekerasan (hb) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| waktu layanan berkelanjutan (Jam / ºC) | - | ≥80 / 1300 | ≥80 / 1300 | ≥80 / 1300 | ≥80 / 1250 | ≥50 / 1350 | ≥50 / 1350 | |
| Struktur mikrografi | Ferit | Ferit | Ferit | Ferit | Ferit | Ferit | Ferit | |
| Sifat magnetik | Magnetik | Magnetik | Magnetik | Magnetik | Magnetik | Magnetik | Magnetik | |